ORIENTENE
MD 35 is designed to provide: |
|
|
|
 |
Consistent
processability. |
|
|
Good
processability. |
|
|
Good
mold filling. |
|
 |
PROPERTIES |
|
VALUE |
|
UNIT
|
|
TEST
METHOD |
 |
|
Melt
Flow ( 230 °C /2.16 Kg) |
|
35 |
|
g/10
min. |
|
ASTM
D-1238, ISO 1133 |
|
|
Density
@ 23 °C |
|
0.9050 |
|
g/cm |
3 |
|
ASTM
D-1505, ISO R 1183 |
|
|
Tensile
Strength @ Yield ( 50 mm/min.) |
|
35 |
|
MPa |
|
ASTM
D-638* |
|
|
Tensile
elongation @ Yield ( 50 mm/min.) |
|
7 |
|
% |
|
ASTM
D-638* |
|
|
Flexural
modulus(1% Secant), at 1.3 mm/min. |
|
1350 |
|
MPa |
|
D
709 A* |
|
|
Notched
Izod impact @ 23 °C |
|
24 |
|
J/m |
|
D
256* |
|
|
Heat
deflection temp. @455 KPa |
|
104
|
|
°C |
|
D
648 |
|
 |
|
|
|
|
|
|
|
 |
|
|
| *
ASTM D638 Molded and tested in accordance with D4101 |
|
| Note: |
|
|
|
The
values given in this technical data sheet are the
results of tests carried out in accordance with
standard test procedures. They are given as indication
to enable customers to make the best use of our
products but must be considered as average values
provided without implying any undertaking on our
part.
|
|
|
Data
should not be used for specification work. |
| |
|
|